Garnet powder, manufacturing method thereof, solid electrolyte sheet using hot press and manufacturing method thereof

ABSTRACT

The present disclosure relates to garnet powder, a manufacturing method thereof, a solid electrolyte sheet using a hot press, and a manufacturing method thereof. In particular, the present disclosure provides a method for manufacturing Li 7 La 3 Zr 2 O 12  (LLZ) garnet powder including preparing a mixture by first dry mixing Li 2 CO 3 , La 2 O 3 , ZrO 2 , and Al 2 O 3 . The mixture is first calcinated for 5 to 7 hours in a temperature range of 800 to 1000° C. The calcinated mixture is ground to a powder with an average particle size of 1 to 4 μm through dry grinding. A cubic-phased LLZ garnet powder is prepared by second calcinating the ground mixture for 10 to 30 hours in a temperature range of 1100 to 1300° C.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims under 35 U.S.C. §119(a) the benefit of Korean Patent Application No. 10-2014-0106858 filed on Aug. 18, 2014, the entire contents of which are incorporated herein by reference.

TECHNICAL FIELD

The present disclosure relates to garnet powder, a manufacturing method thereof, a solid electrolyte sheet using a hot press and a manufacturing method thereof, and in particular, to garnet powder in which the garnet powder is obtained in high yields compared to existing garnet pellets having a very small amount of LLZ (Li₇La₃Zr₂O₁₂) garnet powder, and a solid electrolyte sheet using this garnet powder has a pure cubic-phased crystal structure without impurities by using a hot press process, and is effective in improving ionic conductivity compared to existing solid electrolytes, a manufacturing method of the garnet powder, a solid electrolyte sheet using a hot press, and a manufacturing method of the solid electrolyte sheet.

BACKGROUND

Secondary batteries are batteries that undergo repeated charging and discharging by chemical energy and electric energy being interconverted through the chemical reactions of oxidation and reduction. Secondary batteries generally include four basic elements: an anode, a cathode, a separator, and an electrolyte. Herein, the anode and the cathode are collectively referred to as an electrode, and among the elements forming electrode materials, a material causing the actual reaction is referred to as an active material.

Generally, lithium ion secondary batteries use a liquid electrolyte and an electrolyte including a liquid. However, liquid electrolytes have disadvantages in that they are volatile, and therefore, may present an explosion hazard. In addition, the liquid electrolytes have inferior thermal stability.

Meanwhile, solid state batteries using a solid state electrolyte have low danger of explosion, and also have excellent thermal stability. In addition, when a bi-polar plate is used, high operating voltage may be obtained by a series connection through electrode lamination, and in this case, higher energy density may be obtained compared to the energy density in a series connection mode of cells using a liquid electrolyte.

In order to prepare such an all solid state battery, a solid electrolyte transferring lithium ions is necessary. Solid electrolytes are largely divided into an organic (polymer) electrolyte and an inorganic electrolyte. The inorganic electrolyte is further divided into an oxide-type electrolyte and a sulfide-type electrolyte.

Of these, the oxide-type solid electrolyte is an oxygen-including electrolyte, such as a LiPON-type, a perovskite-type, a garnet-type and a glass ceramic-type. Oxide-type solid electrolytes have an ionic conductivity of 10⁻⁵ to 10⁻³ S/cm lower than sulfide-based electrolytes. The oxide-type solid electrolyte, however, has advantages in that the oxide-type solid electrolyte is stable with respect to moisture and the reactivity in the atmosphere due to oxygen is low, as compared to the sulfide-type solid electrolyte.

The oxide-based solid electrolyte has high grain boundary resistance, and therefore, an electrolyte membrane or pellets, in which necking between the particles are formed from high temperature sintering, may be used, and there is a problem in that mass productivity is very low to form a large-area electrolyte membrane since high temperature sintering is carried out at a temperature of 900 to 1400° C.

Particularly, a garnet-type solid electrolyte requires a long time of 6 hours or longer at a high temperature of 1000 to 1200° C. in final calcination, and in order to prevent lithium volatilization, and to secure phase changes and composition uniformity, pellet-covered garnet may be used. However, there is a disadvantage in that the proportion of garnet secured using such pellets is usually less than 20% by weight with respect to the total weight, which is a very small amount.

The US Patent Application Publication No. 2013-0344416 discloses solid oxide ceramics prepared by hot pressing pellets that are prepared including lithium carbonate, lanthanum hydroxide, zirconium oxide, and alumina; however, there is a disadvantage in that pellet-type LLZ with low crystallizability is formed.

Accordingly, in order to secure a large amount of garnet powder, much research has been conducted, including basic physical property studies, preparation of garnet sheet, preparation of a complex solid electrolyte of garnet and polymers, and studies on the materials capable of being utilized in the manufacturing process of all solid state batteries.

The above information disclosed in this Background section is only for enhancement of understanding of the background of the invention and therefore it may contain information that does not form the prior art that is already known in this country to a person of ordinary skill in the art.

SUMMARY

The present disclosure has been made in an effort to solve the above-described problems associated with the prior art. The inventors of the present disclosure have found that garnet powder may have a pure cubic-phased crystal structure with high crystallizability while being produced in a higher yield. By manufacturing a solid electrolyte sheet using this garnet powder through a hot press process, the solid electrolyte sheet may have improved ionic conductivity compared to existing solid electrolytes. Accordingly, in an embodiment of the present disclosure a garnet powder having a cubic-phased crystal structure is provided.

In another embodiment of the present disclosure a method for manufacturing the garnet powder in an improved yield compared to existing garnet pellets is provided.

In another embodiment of the present disclosure a solid electrolyte sheet including the garnet powder, which has improved ionic conductivity, is provided.

In another embodiment of the present disclosure a method for manufacturing the solid electrolyte sheet using a hot press is provided.

Another embodiment of the present disclosure provides LLZ (Li₇La₃Zr₂O₁₂) garnet powder having a cubic-phased crystal structure, wherein a molar ratio of the Li:La:Zr atoms is 6.5 to 8.3 mol:3 mol:2 mol.

In another embodiment, the present disclosure provides a method for manufacturing LLZ (Li₇La₃Zr₂O₁₂) garnet powder including preparing a mixture by first dry mixing Li₂CO₃, La₂O₃, ZrO₂, and Al₂O₃; and the mixture is first calcinated for 5 to 7 hours in a temperature range of 800 to 1000° C. The calcinated mixture is ground to a powder size of 1 to 4 μm through dry grinding. A cubic-phase LLZ (Li₇La₃Zr₂O₁₂) garnet powder is prepared by second calcinating the ground mixture for 10 to 30 hours in a temperature range of 1100 to 1300° C.

In another embodiment, the present disclosure provides a solid electrolyte sheet including the LLZ (Li₇La₃Zr₂O₁₂) garnet powder.

In a further embodiment, the present disclosure provides a method for manufacturing a solid electrolyte sheet using a hot press including preparing the LLZ (Li₇La₃Zr₂O₁₂) garnet powder; and manufacturing a solid electrolyte sheet by hot pressing the garnet powder for 30 minutes to 2 hours in a temperature range of 1050 to 1250° C. under an argon atmosphere.

Other aspects and embodiments of the invention are discussed infra.

LLZ (Li₇La₃Zr₂O₁₂) garnet powder according to the present disclosure is prepared through a two-step calcination processes as a powder itself. As a result, the obtained garnet powder content is high compared to existing garnet pellets having a very small amount of garnet powder, and the prepared LLZ garnet powder has a cubic-phased crystal structure with high crystallizability.

In addition, a solid electrolyte sheet including the LLZ (Li₇La₃Zr₂O₁₂) garnet powder according to the present disclosure uses a hot press process, therefore, a solid electrolyte sheet having a pure cubic-phased crystal structure may be manufactured without including impurities, and the solid electrolyte sheet is effective in improving ionic conductivity compared to existing solid electrolytes.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features of the present disclosure will now be described in detail with reference to certain exemplary embodiments thereof illustrated in the accompanying drawings which are given hereinbelow by way of illustration only, and thus are not limitative of the present disclosure.

FIG. 1 illustrates XRD measurement results of garnet powder manufactured in Example 1 and Comparative Examples 1 to 3 of the present disclosure.

FIG. 2A is a Raman measurement result of garnet powder manufactured in Example 1 of the present disclosure.

FIG. 2B is a Raman measurement result of garnet powder manufactured in Comparative Example 1 of the present disclosure.

FIG. 2C is a Raman measurement result of garnet powder manufactured in Comparative Example 2 of the present disclosure.

FIG. 2D is a Raman measurement result of garnet powder manufactured in Comparative Example 3 of the present disclosure.

FIG. 3 shows ICP measurement results of garnet powder manufactured in Example 1 and Comparative Examples 1 to 3 of the present disclosure.

FIG. 4 is an SEM picture of garnet powder manufactured in Example 1 of the present disclosure.

FIG. 5 is a graph showing density and ionic conductivity of solid electrolyte sheets prepared in Example 2 and Comparative Examples 4 and 5 of the present disclosure.

FIG. 6 is XRD measurement results of solid electrolyte sheets prepared in Examples 1 and 2 and Comparative Examples 4 and 5 of the present disclosure.

FIGS. 7A-7C are Raman measurement results of solid electrolyte sheets prepared in Example 2 and Comparative Examples 4 and 5 of the present disclosure.

FIGS. 8A-8C are SEM pictures of solid electrolyte sheets prepared in Example 2 and Comparative Examples 4 and 5 of the present disclosure.

It should be understood that the appended drawings are not necessarily to scale, presenting a somewhat simplified representation of various preferred features illustrative of the basic principles of the invention. The specific design features of the present disclosure as disclosed herein, including, for example, specific dimensions, orientations, locations, and shapes will be determined in part by the particular intended application and use environment.

In the figures, reference numbers refer to the same or equivalent parts of the present disclosure throughout the several figures of the drawing.

DETAILED DESCRIPTION

Hereinafter reference will now be made in detail to various embodiments of the present disclosure, examples of which are illustrated in the accompanying drawings and described below. While the invention will be described in conjunction with exemplary embodiments, it will be understood that present description is not intended to limit the invention to those exemplary embodiments. On the contrary, the invention is intended to cover not only the exemplary embodiments, but also various alternatives, modifications, equivalents and other embodiments, which may be included within the spirit and scope of the invention as defined by the appended claims.

The present disclosure provides LLZ (Li₇La₃Zr₂O₁₂) garnet powder having a cubic-phased crystal structure in which the molar ratio of the Li:La:Zr atoms is 6.5 to 8.3:3:2.

The LLZ (Li₇La₃Zr₂O₁₂) garnet powder is divided into cubic-phased or tetragonal-phased, and herein, the cubic-phased is reported to have excellent ionic conductivity of 100 times or higher with the cubic-phased having ionic conductivity of approximately 10⁻⁴ S/cm and the tetragonal-phased having ionic conductivity of approximately 10⁻⁶ S/cm. Accordingly, synthesizing to have a cubic-phased crystal structure instead of impurities, secondary-phased or tetragonal-phased is advantageous in improving the physical properties.

In embodiments of the LLZ garnet powder, the molar ratio of the Li atom ranges from 6.5 to 8.3 mol. When the molar ratio is less than 6.5 mol, garnet powder having a cubic-phased crystal structure is not produced, and when the molar ratio is greater than 8.3 mol, there is a problem in that ionic conductivity rapidly decreases due to the presence of impurities. Generally, Li volatilization most actively occurs at a temperature of approximately 900° C. or higher, therefore, the Li atom may be used in greater than 10 mol %. In a certain embodiment, the molar ratio of the Li:La:Zr atoms is preferably 7:3:2.

In certain embodiments, some of the Li of the LLZ garnet powder may be substituted with Al. Herein, the Al stabilizes the cubic-phased crystal structure and affects the density increase with a liquid phase sintering effect, and may improve the ionic conductivity of the powder. Consequently, some of the Li may be substituted with Al in the synthesis.

The Al may be substituted in a range of 0.02 to 1.075 mol. The Al may be doped in the form of Al₂O₃ at 0.1 to 5% by weight with respect to the LLZ. Specifically, when the Al₂O₃ is doped in less than 0.1% by weight, physical properties of a solid electrolyte may be degraded, and when in doped greater than 5% by weight, there is a problem in that impurities (Al₃Zr, Li₂ZrO₃) are produced with the cubic-phased powder. In a certain embodiment, the Al₂O₃ is doped at 3.69% by weight.

In addition, the present disclosure provides a method for manufacturing LLZ (Li₇La₃Zr₂O₁₂) garnet powder including preparing a mixture by first dry mixing Li₂CO₃, La₂O₃, ZrO₂, and Al₂O₃. The mixture is first calcinated for 5 to 7 hours in a temperature range of 800 to 1000° C. The calcinated mixture is ground to a powder with an average particle size of 1 to 4 μm through dry grinding. The cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder is prepared by second calcinating the grinded mixture for 10 to 30 hours in a temperature range of 1100 to 1300° C.

The operation of preparing a mixture by first dry mixing is an operation of simply mixing raw material powders, and no energy is transferred to the powders in the process. There may be a 5 minute rest time in each step to prevent the transfer of heat energy into the powders. The mixing method includes a dry method or a wet method. Dry mixing using a planetary mill owned by the inventors may be carried out since, in the case of wet mixing, the process time may increase, (such as by one day or more to dry the mixture) and side reactions due to solvents may occur. As the mixing condition, the planetary milling condition is milder, and the number of zirconia balls may be approximately half when compared to the two-step dry mixing.

In the LLZ garnet powder, the molar ratio of the Li₂CO₃, La₂O₃, ZrO₂, and Al₂O₃ is 6.5 to 8.3 mol:3 mol:4 mol 0.02 to 1.075 mol.

In the LLZ garnet powder, some of the Li may be substituted with Al. The substituted Al may be Al₂O₃ being doped in 0.1 to 5% by weight with respect to the LLZ.

The operation of first calcinating the mixture may be carried out for 5 to 7 hours in a temperature range of 800 to 1000° C. In this operation, CO₂ and H₂O residues present inside the mixture powder are removed. Particularly, when a carbonic acid component of the Li₂CO₃ is not removed, the carbonic acid component remains inside the LLZ garnet powder, and becomes a factor causing a decrease of density and ionic conductivity, therefore, CO₂ needs to be removed. Calcination may be carried out for 6 hours at 900° C.

In the operation of grinding the calcinated mixture to a powder size of 1 to 4 μm through dry grinding, some of the calcinated mixture may be firmly aggregated, and some may experience a phase shift of the garnet structure. Consequently, when performing the final calcination process, milling may be carried out under a mixing condition stronger than the first calcination step in order to simultaneously have the crushing of the aggregated powder and the powder mixing for maximizing the reaction, and the number of zirconia balls may be approximately twice compared to the first calcination step.

In the operation of preparing cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder by second calcinating the grinded mixture for 10 to 30 hours in a temperature range of 1100 to 1300° C., the temperature and the time for producing the LLZ garnet powder may be different depending on the composition of the raw materials. Particularly, in the case of the raw materials including hydroxide, the operation may be carried out in a low temperature range of 50 to 100° C.

The method for manufacturing the LLZ garnet powder may further include an operation of analyzing the LLZ garnet powder, and the analysis may be carried out using X-Ray Diffraction (XRD), Raman Spectroscopy, or Inductively Coupled Plasma Mass Spectrometry (ICP-MS). The XRD may identify the LLZ phase and impurities, and through the Raman, phases and impurities corresponding to regions having hundreds of micrometers or less, which are difficult to be determined with XRD, may be identified. In addition, using ICP, differences between target compositions and synthesized compositions may be compared by identifying the ratio of each atom composition in the LLZ.

In addition, the present disclosure provides a solid electrolyte sheet including the LLZ (Li₇La₃Zr₂O₁₂) garnet powder. The solid electrolyte sheet may have a pure cubic-phased crystal structure without including impurities, and have improved ionic conductivity as a solid electrolyte sheet in a powder phase compared to existing solid electrolytes in a pellet phase.

In addition, the present disclosure provides a method for manufacturing a solid electrolyte sheet using a hot press including preparing the LLZ (Li₇La₃Zr₂O₁₂) garnet powder; and manufacturing a solid electrolyte sheet by hot pressing the garnet powder for 30 minutes to 2 hours in a temperature range of 1050 to 1250° C. under argon atmosphere.

In the operation of manufacturing a solid electrolyte sheet using a hot press, when the temperature is lower than 1050° C., a tetragonal phase that is produced advantageously at low temperature may be formed, and when the temperature is higher than 1250° C., an impurity phase such as pyrochlore (La₂Zr₂O₇) may be formed, or melting of the garnet powder may occur.

The solid electrolyte sheet may have a thickness of 0.01 to 5 mm. Specifically, when the thickness of the solid electrolyte sheet is less than 0.01 mm, cracks or fractures may occur due to the weak physical properties, and when greater than 5 mm, the energy density of a battery cell may greatly decrease due to the weight of the solid electrolyte.

In the solid electrolyte sheet, almost 100% of the powder used may be manufactured to a sheet, and the solid electrolyte sheet has ionic conductivity ranging from 6×10⁻⁴ to 10×10⁻⁴ S/cm.

The method for manufacturing the solid electrolyte sheet may further include an operation of analyzing the solid electrolyte sheet, and the analysis may be carried out using X-Ray Diffraction (XRD), Raman Spectroscopy, or Inductively Coupled Plasma Mass Spectrometry (ICP-MS).

Consequently, the garnet powder according to the present disclosure may be prepared as powder through a two-step calcination process. Therefore, the obtained content of the garnet powder is high compared to existing garnet pellets including a very small amount of garnet powder, and the prepared garnet powder has a cubic-phased crystal structure with high crystallizability.

In addition, the solid electrolyte sheet including the LLZ (Li₇La₃Zr₂O₁₂) garnet powder according to the present disclosure may use a hot press process. Therefore, a solid electrolyte sheet having a pure cubic-phased crystal structure may be manufactured without including impurities, and the solid electrolyte sheet is effective in improving ionic conductivity compared to existing solid electrolytes.

EXAMPLES

Hereinafter, the present disclosure will be described in more detail with reference to examples, however, the scope of the present disclosure is not limited to the following examples.

Manufacture of Garnet Powder Example 1

A mixture was prepared by first dry mixing Li₂CO₃, La₂O₃, ZrO₂ and Al₂O₃, which are raw materials, in a molar ratio of 7.7:3:4:0.5. Next, the mixture was first calcinated for 6 hours at 900° C., and then the powder was ground to an average particle size of 1 to 4 μm. The ground mixture was second calcinated for 20 hours at 1200° C., and cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder was obtained.

Comparative Example 1

LLZ (Li₇La₃Zr₂O₁₂) garnet powder was obtained by grinding and calcinating a mixture in the same manner as in Example 1 except that the mixture was prepared by first dry mixing LiOH, La₂O₃, ZrO₂, and Al₂O₃, which are raw materials, in a molar ratio of 15.4:3:4:0.5.

Comparative Example 2

LLZ (Li₇La₃Zr₂O₁₂) garnet powder was obtained by grinding and calcinating a mixture in the same manner as in Example 1 except that the mixture was prepared by first dry mixing LiOH, La(OH)₃, ZrO₂, and Al₂O₃, which are raw materials, in a molar ratio of 15.4:6:4:0.5.

Comparative Example 3

LLZ (Li₇La₃Zr₂O₁₂) garnet powder was obtained by grinding and calcinating a mixture in the same manner as in Example 1 except that the mixture was prepared by first dry mixing Li₂CO₃, La(OH)₃, ZrO₂, and Al₂O₃, which are raw materials, in a molar ratio of 7.7:6:4:0.5.

Manufacture of Solid Electrolyte Sheet Example 2

A solid electrolyte sheet was manufactured by hot pressing the cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder manufactured in Example 1 for 1 hour at a temperature of 1100° C. under argon (Ar) atmosphere. Herein, the process was carried out under a pressure of 50 MPa, and the solid electrolyte sheet was manufactured to a thickness of 5 mm and a size of 30×30 mm².

Comparative Example 4

A solid electrolyte sheet was manufactured in the same manner as in Example 2 except that the cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder manufactured in Example 1 was hot pressed for 1 hour at a temperature of 900° C. under argon (Ar) atmosphere.

Comparative Example 5

A solid electrolyte sheet was manufactured in the same manner as in Example 2 except that the cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder manufactured in Example 1 was hot pressed for 1 hour at a temperature of 1000° C. under argon (Ar) atmosphere.

Comparative Example 6

A solid electrolyte sheet was manufactured by preparing LLZ (Li₇La₃Zr₂O₁₂) garnet pellets using a general process, and then calcinating the pellets again. In the solid electrolyte sheet, the garnet pellets were prepared by being first calcinated for 6 hours at a temperature of 900° C. and then applying a pressure of 130 MPa thereto, and then the solid electrolyte sheet was manufactured by second calcinating the pellets again for 20 hours at a temperature of 1200° C.

Test Example 1 X-Ray Diffraction (XRD) Measurements of Garnet Powder Manufactured in Example 1 and Comparative Examples 1 to 3

In order to identify the composition and the crystallizability of the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3, peaks were analyzed using an XRD device, and the results are shown in FIG. 1.

FIG. 1 shows the XRD measurement results of the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3. As identified in FIG. 1, impurities were observed in all the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3, however, it was seen that the amount of the impurities is small in the examples considering the small impurity peaks observed in the examples including La₂O₃, compared to Comparative Examples 2 and 3 including La(OH)₃ in which relatively large impurity peaks were observed.

Test Example 2 Raman Spectroscopy Measurements of Garnet Powder Manufactured in Example 1 and Comparative Examples 1 to 3

In order to identify the crystal phase and the impurities of the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3, peaks were analyzed using a Raman Spectroscopy device, and the results are shown in FIGS. 2A to 2D.

FIG. 2A shows the Raman measurement result of the garnet powder manufactured in Example 1, FIG. 2B shows the Raman measurement result of the garnet powder manufactured in Comparative Example 1, and FIG. 2C shows the Raman measurement result of the garnet powder manufactured in Comparative Example 2. In addition, FIG. 2D shows the Raman measurement result of the garnet powder manufactured in Comparative Example 3.

As identified in FIGS. 2A to 2D, the appearance of impurity peaks instead of the cubic garnet peaks was identified in Comparative Examples 2 and 3 while only cubic garnet peaks were observed in Comparative Example 1, and it was identified that, in Example 1, the formed graph was from cubic garnet although a small amount of impurities was observed.

Test Example 3 Inductively Coupled Plasma Mass Spectrometry (ICP-MS) Measurements of Garnet Powder Manufactured in Example 1 and Comparative Examples 1 to 3

In order to identify the lithium content (mol) of the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3, analysis was carried out using an ICP-MS device, and the results are shown in FIGS. 3 and 4.

FIG. 3 shows the ICP measurement results of the garnet powder manufactured in Example 1 and Comparative Examples 1 to 3. It was identified that, in the garnet synthesis, an impurity phase was formed when Li is included in 6 mol or less, therefore, the example including La₂O₃ and Li₂CO₃ with 6 mol or higher of Li forming a stable garnet phase was advantageous in the garnet powder process.

FIG. 4 is an SEM picture of the garnet powder manufactured in Example 1. As shown in FIG. 4, the formation of the garnet powder having particle sizes of a few to tens of μm was identified.

In conclusion, based on the XRD, the Raman and the ICP analysis results carried out in Text Examples 1 to 3, it was demonstrated that the garnet powder of Example 1 including La₂O₃ and Li₂CO₃ is advantageous.

Test Example 4 Density and Ionic Conductivity Measurements of Garnet Powder Manufactured in Example 2 and Comparative Examples 4 to 6

The density and the ionic conductivity of the garnet powder manufactured in Example 2 and Comparative Examples 4 to 6 were measured, and the results are shown in the following Table 1.

TABLE 1 Category Density (%) Ionic conductivity(S/cm) Example 2 98 8.7 × 10⁻⁴ Comparative Example 4 82 9.1 × 10⁻⁶ Comparative Example 5 93 7.3 × 10⁻⁵ Comparative Example 6 85   1 × 10⁻⁴

As shown in Table 1, it was identified that the garnet manufactured in Example 2 had significantly superior density and ionic conductivity compared to the garnet manufactured in Comparative Examples 4 to 6. Particularly, the ionic conductivity in Example 2 carrying out the hot press process at 1100° C. was superior to the ionic conductivity in Comparative Examples 4 and 5 carrying out the hot press process at temperatures of 900° C. and 1000° C.

FIG. 5 is a graph showing the density and the ionic conductivity of the solid electrolyte sheet manufactured in Example 2 and Comparative Examples 4 and 5. As identified in FIG. 5, it was seen that general relative density when the pellet was prepared and then calcinated was approximately 85%, and the ionic conductivity was approximately 1×10⁻⁴ S/cm. Meanwhile, in the hot press process using the garnet powder, the density increased as the process temperature increased, and the ionic conductivity also increased as well. Consequently, it was identified that maximum ionic conductivity was obtained in Example 2 carrying out the hot press process at a temperature of 1100° C. However, at process temperatures of 1250° C. or higher, an impurity phase may be formed or some of the garnet powder may be melted.

Test Example 5 X-Ray Diffraction (XRD) Measurements of Garnet Powder Manufactured in Examples 1 and 2, and Comparative Examples 4 and 5

In order to identify the particle crystallizability and the presence of impurities of the garnet powder manufactured in Examples 1 and 2, and Comparative Examples 4 and 5, peaks were analyzed using an XRD device, and the results are shown in FIG. 6.

FIG. 6 shows the XRD measurement results of the solid electrolyte sheet manufactured in Examples 1 and 2, and Comparative Examples 4 and 5. As identified in FIG. 6, it was seen that the garnet powder manufactured in Example 1 had a cubic phase with a small amount of impurities present. Meanwhile, it was identified that the solid electrolyte sheet manufactured in Comparative Examples 4 and 5 carrying out a hot press had a cubic phase with low crystallizability, and the solid electrolyte sheet manufactured in Example 2 had a pure cubic phase with high crystallizability. Based on the above observation, it was identified that the impurities present in the garnet powder manufactured in Example 1 were removed through the hot press process.

Test Example 6 Raman Spectroscopy Measurements of Garnet Powder Manufactured in Example 2, and Comparative Examples 4 and 5

In order to identify the crystal phase and the impurities of the garnet powder manufactured in Example 2 and Comparative Examples 4 and 5, peaks were analyzed using a Raman Spectroscopy device, and the results are shown in FIGS. 7 and 8A-8C.

FIGS. 7A-7C show the Raman measurement results of the solid electrolyte sheet manufactured in Example 2 and Comparative Examples 4 and 5. As identified in FIGS. 7A-7C, a tetragonal phase and a cubic phase were mixed in the solid electrolyte sheet manufactured in Comparative Examples 4 and 5, and impurity peaks were observed. Meanwhile, only cubic-phased peaks were observed in Example 2.

FIGS. 8A-8C are SEM pictures of the solid electrolyte sheet manufactured in Example 2 and Comparative Examples 4 and 5. As identified in FIGS. 8A-8C, it was seen that the size of the particles increased as the temperature of the hot press process increased, and closed pores were observed in Example 2 carrying out the process at 1100° C., and this was a phenomenon due to particle growth. Based on the above observation, it was identified that grain boundary resistance decreased as the particle sizes of the material increased inducing the increase of ionic conductivity.

Consequently, it was identified that the content of the LLZ (Li₇La₃Zr₂O₁₂) garnet powder obtained according to the present disclosure is high, and the garnet powder has a cubic-phased crystal structure with high crystallizability, and by using a hot press process, the solid electrolyte sheet using the garnet powder has a pure cubic-phased crystal structure without impurities, and has improved ionic conductivity compared to existing solid electrolytes.

The invention has been described in detail with reference to preferred embodiments thereof. However, it will be appreciated by those skilled in the art that changes may be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents. 

What is claimed is:
 1. Li₇La₃Zr₂O₁₂ (LLZ) garnet powder having a cubic-phased crystal structure, wherein a molar ratio of the Li:La:Zr atoms is 6.5 to 8.3:3:2.
 2. The LLZ garnet powder of claim 1, wherein some of the Li is substituted with Al.
 3. The LLZ garnet powder of claim 2, wherein the substituted Al is included in 0.02 to 1.075 mol, and the Al is doped in the form of Al₂O₃ in 0.1 to 5% by weight with respect to the LLZ.
 4. A method for manufacturing Li₇La₃Zr₂O₁₂ (LLZ) garnet powder comprising: preparing a mixture by first dry mixing Li₂CO₃, La₂O₃, ZrO₂, and Al₂O₃; first calcinating the mixture for 5 to 7 hours in a temperature range of 800 to 1000° C.; grinding the calcinated mixture to a powder with an average particle size of 1 to 4 μm through dry grinding to form a ground mixture; and preparing a cubic-phased LLZ (Li₇La₃Zr₂O₁₂) garnet powder by second calcinating the ground mixture for 10 to 30 hours in a temperature range of 1100 to 1300° C.
 5. The method for manufacturing LLZ garnet powder of claim 4, wherein, in the LLZ garnet powder, a molar ratio of the Li₂CO₃, the La₂O₃, the ZrO₂, and the Al₂O₃ is 6.5 to 8.3:3:4:0.02 to 1.075.
 6. The method for manufacturing LLZ garnet powder of claim 4, wherein, in the LLZ garnet powder, some of the Li is substituted with Al.
 7. The method for manufacturing LLZ garnet powder of claim 6, wherein the substituted Al by doping Al₂O₃ in 0.1 to 5% by weight with respect to the LLZ.
 8. The method for manufacturing LLZ garnet powder of claim 4 further comprising analyzing the LLZ garnet powder, wherein the analysis is carried out using X-Ray Diffraction (XRD), Raman Spectroscopy, or Inductively Coupled Plasma Mass Spectrometry (ICP-MS).
 9. A solid electrolyte sheet comprising the LLZ garnet powder of claim
 1. 10. A solid electrolyte sheet comprising the LLZ garnet powder of claim
 2. 11. A method for manufacturing a solid electrolyte sheet using a hot press, the method comprising: preparing the LLZ garnet powder of claim 1; and manufacturing a solid electrolyte sheet by hot pressing the garnet powder for 30 minutes to 2 hours in a temperature range of 1050 to 1250° C. under an oxygen free atmosphere.
 12. The method for manufacturing a solid electrolyte sheet of claim 11, wherein a thickness of the solid electrolyte sheet ranges from 0.01 to 5 mm.
 13. The method for manufacturing a solid electrolyte sheet of claim 11, wherein ionic conductivity of the solid electrolyte sheet ranges from 6×10⁻⁴ to 10×10⁻⁴ S/cm.
 14. The method for manufacturing a solid electrolyte sheet of claim 11, further comprising analyzing the solid electrolyte sheet, wherein the analysis is carried out using X-Ray Diffraction (XRD), Raman Spectroscopy, or Inductively Coupled Plasma Mass Spectrometry (ICP-MS).
 15. A method for manufacturing a solid electrolyte sheet using a hot press, the method comprising: preparing the LLZ garnet powder of claim 2; and manufacturing a solid electrolyte sheet by hot pressing the garnet powder for 30 minutes to 2 hours in a temperature range of 1050 to 1250° C. under an oxygen free atmosphere.
 16. The method for manufacturing a solid electrolyte sheet of claim 15, wherein a thickness of the solid electrolyte sheet ranges from 0.01 to 5 mm.
 17. The method for manufacturing a solid electrolyte sheet of claim 15, wherein ionic conductivity of the solid electrolyte sheet ranges from 6×10⁻⁴ to 10×10⁻⁴ S/cm.
 18. The method for manufacturing a solid electrolyte sheet of claim 15, further comprising analyzing the solid electrolyte sheet, wherein the analysis is carried out using X-Ray Diffraction (XRD), Raman Spectroscopy, or Inductively Coupled Plasma Mass Spectrometry (ICP-MS). 